|General Refractory Products|Fire clay and high alumna brick for hot-blast stoves|Coke oven refractory bricks|Refractory bricks for blast furnace|Refractory for pretreatment of hot metal|High alumni bricks for electric arc furnace roofs|Refractory Bricks for circling furnace and refining furnace|Ladle|Con-casting refractory products|Refractory for teeming|Monolithic refractory& Others|  
Monolithic refractory & Others
High-Performance Refractory Castable
　　　　　Brand







Item		 Heavy Weight High Performance Refractory Castable
Light Weight High Performance Castable		 Clay Bonding High Performance Refractory Castable
Corundum Corundum-Mullite High-Alumina Fire-clay Corundum Corundum -Mullite High-Alumina Fire-clay
A-90 A-75 A-70 A-40 QA-90 QA-70 QA-60 QA-40 JN-1500 JN-1600
AL2O3 % ≧90 ≧75 ≧70 ≧40 ≧90 ≧70 ≧60 ≧40 ≧50 ≧70
Refractoriness℃ ≧1790 ≧1790 ≧1750 ≧1730 ≧1790 ≧1790 ≧1750 ≧1700 Sio2≦40 Sio2≦25
Bulk density g/cm3 ≧2.9 ≧2.5 ≧2.4 ≧2.2 0.8-1.8 0.8-1.6 0.6-1.4 0.6-1.4 ≧2.3 ≧2.4
Cold
Crushing strength Mpa		 110℃×24h ≧50 ≧50 ≧50 ≧40 5-15 5-15 3-13 3-13    
1500℃×24h ≧8 ≧8 ≧8 ≧8         2-5 2-5
Modulus of rupture Mpa 110℃×24h ≧10 ≧10 ≧10 ≧10         ≧10 ≧10
1500℃×24h         0.4-0.6 0.4-0.6 0.3-0.5 0.3-0.5    
Thermal conductivity W(m.k)(300℃+_25℃)                 -0.2-0 -0.2-0
Linear change after heating % 110℃×24h                    
1500℃×3h +_0.5 +_0.5 +_0.5 1400℃×3h+_0.5 +_0.6 +_0.6 1450℃×3h+_0.5 1300℃×3h+_0.5 -0.2-+0.5 -0.2-+0.5
Max service temperature ℃ 1700 1600 1500 1400 1700 1650 1450 1350 1500 1600
Application Used at every kind industrial kiln. According to the concrete conditions, we manufacture low-cement castable,ultra-low-cement castable,self-flowing castable and Break resistance castable. Installation method: Vibrating and self-flowing. For neutral-or Oxidation-Atmosphere industrial kiln lining, Good insulation property. For steel-making heating furnace.Soaking pits and other industrial frunace. High refractoriness and good impact resistance Installation method.vibrating.
|Abrasion Resistance High-strength and Insulation Castable|
　　　　　Brand






Item		 High Abrasion Resistance Lining Castable Medium Abrasion Resistance Lining Castable Abrasion Resistance and Insulation Castable Insulation Lining Castable High-strength Abrasion Resistance Castable for Hot-electical Industry
JM-2.9 ZM-2.1 QM-1.3 QM-1.1 QM-0.9 JM-2.5 JM-2.7
AL2O3% ≧80         ≧70 ≧80
FE2O3% ≦1.5   （500℃）≦0.4W.（M.K）Thermal conductivity （500℃）≦0.28W.（M.K）Thermal conductivity （500℃）≦0.26W.（M.K）Thermal conductivity ≦2.0 ≦1.5
Bulk densityg/cm3 ≧2900 ≧2100 ≧1300 ≦1100 ≧900 ≧2.5 ≧2.7

Cold crushing strength

Modulus of rupture

Mpa

 110℃×24h 80-120/18-20 50-80/7-9 10-20/4-8 4-7/1.5-3 2-5/1-2 40-60/10-15 60-80/14-18
540℃×3h 70-100/24-28 40-60/6-8 8-18/4-7 4-7/1.5-3 2-5/1-2 40-60/10-15 60-80/14-18
815℃×3h 80-120/26-32 50-80/6-10 8-18/4-7 4-7/1.5-3.5 2-4/1-2 60-80/12-17 80-100/16-20

Permanent linear change after heating		 ≦-0.2 ≦-0.2 -0.2-0 -0.25-0 -0.3-0 ≦-0.2 ≦-0.15

Using explain		 For abrasion resistance lining of chemical industry use.Excellent abration resistance and high strength installation method:casting and paint.Max service temperature.1500℃ For chemical industry furnace lining where the abrasion is not serious.Installation method:hand painting or casting 1400℃ For insulation lining of thermal industry equipment use. Installation method:casting or painting. For insulation lining where the abrasion is serious.Installation method: casting or painting. For chemical industry lining furnace where the abrasion is not serious.Installation method:hand painting or casting. For the lining of hot-electrical industry. Excellent abrasion resistance and high strength installation method:vibrating.
Castable for Blast Furnace Taphole, Alumium-spinel Castable and High-Alumina Plastic Material
　　　　　　　　　　Brand
Item		 Castable for Blast-furnace Taphole Alumina-Spinel Castable
High-Alumina Plastic Material
TG-11 TG-12 TG-13 TG-14 AM-70 AM-85 JS-1500 JS-1600
AL2O3% ≧60 ≧50 ≧45 ≧45 ≧70 ≧85 ≧55 ≧65
SIC+C% ≧12 ≧30 ≧7 ≧12 MGO≦12 MGO≦10 SIO2≦40 SIO2≦30
CAO% ≦1.5 ≦1.5 ≦1.5 ≦1.5        

Bulk density

g/cm3

 110℃×24h ≧2.7 ≧2.6 ≧2.4 ≧2.4 ≧2.8 ≧3.0 ≧2.3 ≧2.4
1000℃×3h         ≧2.7 ≧2.9    
1450℃×3h ≧2.6 ≧2.5 ≧2.35 ≧2.35 1500℃×3h≧2.9 1500℃×3h≧3.1    

Crushing strength

Mpa

 110℃×24h ≧30 ≧20 ≧30 ≧20        
1450℃×3h ≧40 ≧30 ≧40 ≧30        

Modulus of rupture

Mpa

 110℃×24h ≧5 ≧4 ≧5 ≧4 ≧5 ≧6 5-7 5-8
1000℃×3h         ≧8 ≧8    
1450℃×3h ≧5 ≧5 ≧6 ≧5 1500℃×3h≧10 1500℃×3h≧12 1500℃×3h≧10 1500℃×3h≧12

Linear change after heating

%

 110℃×24h         0-0.1 0--0.1 -0.2-0 -0.2-0
1000℃×3h         0-+0.2 0-+0.2    
1450℃×3h +_0.5 +_0.5 +_0.6 +_0.6 1500℃×3h
0-+0.8		 1500℃×3h
0-+0.8		 1500℃×3h
0-+0.5		 1500℃×3h
0-+0.5
Max service temperature℃         1760 1800 1500 1600
Using explain Taphole hot-metal line Taphole slag line Hot-metal Taphole Slag taphole For lining of ladle. Excellent property of corrosion resistance and spalling resistance. Installation method:vibrating casting For lining of steel rolling,lncineration kiln and other industrial furnace. Excellent spalling resistance and high refractoriness.
Others
（1）Refractory for construction （2） Special cement
A.Ready-made products B. Special cement C．Hollow ball
 