Con-casting

| Refractory Products|Refractory raw materials|

Alumna-zircon-graphite products A. Sub-entry nozzle, slag line B. Monoblock stopper C. Ladle shroud

Sub-entry nozzle

	ARG	ASN
AL203%>	40	43.0
F.C.%>	26.0	24
Bulk Density g/cm³	2.25	2.28
Apparent Porosity%<	19.0	18.5
Cold Crushing Strength.Mpa.>	19.0	18.5
Thermal Shock Resistance.Times>	5	5

slag line

	Z45	ZSP
Zr02%	75.0	70.0
F.C.%>	11.0	15.0
Bulk Density g/cm³	3.50	3.40
Apparent Porosity%<	22.05	21.5
Cold Crushing Strength.Mpa.>	16.0	18.0

Monoblock stopper

	ASH HEAD	ASR BODY	ANC HEAD	MT HEAD
AL203%>	56.0	44.0	58.0
F.C.%>	19.0	23.0	15.0	19.0
Mg 0%				58.0
Bulk Density g/cm³	2.44	2.36	2.64	2.50
Apparent Porosity%<	19.0	17.0	16.0	18.0
Cold Crushing Strength.Mpa.>	20.0	16.0	16.0	15.0
Thermal Shock Resistance.Times>	3	3	3	3

Ladle shroud

	ALP PREHEATING	ALG NON-PREHEATING
AL203%>	41.0	34
F.C.%>	30.0	27
Zr02	3.0	3
Bulk Density g/cm³	2.16	2.13
Apparent Porosity%<	19.0	19.5
Cold Crushing Strength.Mpa.>	18.0	17.5
Thermal Shock Resistance.Times>	5	5

Silica products

	Ladle shroud	Sub-entry nozzle
Sio%>	99	99
Bulk Density g/cm³	1.85	1.89
Apparent Porosity%<	15	14.5
Cold Crushing Strength.Mpa.>	45	46
Thermal Shock Resistance.Times>	5	5

Zircon sizing nozzle

Brand	F-75	F-70	Z-75	Z-70	X-75	WL-60
AL₂O₃%
Z_r O₂ %	75.5	71	75	71	75
% Apparent Porosity	18	17	18	17	18	21
G/cm³ Bulk Density	4.00	3.90	4.00	3.90	4.00

Permeability refractory products

Brand	TL-60	TL-85	TL-92	TL-95
AL₂O₃%	61	85	92	95
Refractoriness	1770	1790	1850	1850
% Apparent Porosity	25-30	25-30	17	24-30
G/cm³ Bulk Density	2.27	2.27	2.50	2.30
NI/min Permeability	25	25	120	80
Model	common	common	common	Explorer-associated

Others A. Taphole sleeve B. Sliding gate bricks

Taphole sleeve

	MT-10A	MT-14A	MT-18A
Mg O%>	80	76	72
F.C.%>	10	14	18
Bulk Density g/cm³	2.90	2.90	2.82
Apparent Porosity%<	4	4	4
Cold Crushing Strength.Mpa.>	40	40	35

Sliding gate bricks

　　　　　　　　　　　　　Brand

Item

Sliding Plate

Nozzle Brick

Well Bricks

AL₂O₃

Sliding Plate

HBL-65

HBL-55

HKL-65

HKL-55

HZL-65

HZL-55

AL₂O₃%

≧65

≧55

≧65

≧55

≧65

≧55

≧65 　

Refractoriness ℃

≧1770

≧1750

≧1770

≧1750

≧1770

≧1750

C≧8 　

Apparent Porosity%

Impregnated & distilled

≦16

Impregnated

≦8

≦9

Unimpregnated

≦23

≦25

Cold crushing strengthMPa

Impregnated & distilled

≧58.8

≧88.2

Impregnated

≧68.8

≧39.2

Unimpregnated

≧24.5

Cold modulus of rupture Mpa Mpa

≧15

Application

Casting or Continuous Casting